Products data sheet for MATTE PET FILM
|
ITEM |
UNIT |
TYPE |
method | |||||
| SFLMK |
SFMK |
SFSM |
SFUMR | |||||
| Feature | rough surface ,low gloss and high haze | |||||||
| Application | transfer ,stamping foil, stamping clothes, stamping leather, metallization and lamination ,label and off-line coated silicone, etc | |||||||
|
Thicknesss |
-MD |
μm |
19 |
19 |
19 |
19 |
DIN
53 370 | |
|
Tensile strength |
-MD |
N/mm2 |
170 |
170 |
170 |
150 |
DIN
53 455 | |
|
-TD |
N/mm2 |
170 |
170 |
170 |
150 |
DIN
53 455 | ||
|
Elongation at break |
-MD |
% |
50 | 50 | 50 |
50 |
DIN
53 455 | |
|
-TD |
% |
50 | 50 | 50 |
50 |
DIN
53 455 | ||
|
shrinkage |
150℃ 15min |
-MD |
% |
2.0 | 2.0 | 2.0 |
2.0 |
BMS
TT 11 |
|
-TD |
% |
0.3 | 0.3 | 0.3 |
0.3 |
BMS
TT 11 | ||
|
Haze |
A |
% |
73±3 | 86±3 | 90±3 |
95±3 |
ASTM D 1003 | |
|
Gloss |
60° |
% |
33±3 | 23±3 | 21±3 |
17±3 |
ASTM D 2457 | |
|
Item |
Unit |
Type |
Method | ||||||
SFWW |
|||||||||
| Feature | low light transit and good shielding ,excellent lamination and printing properties | ||||||||
| Application | pakage lamination, label for diary used products and tire and battery and electronic products | ||||||||
|
Thicknesss |
-MD |
μm |
12 |
25 |
38 |
50 |
72 |
DIN
53 370 | |
|
Tensile strength |
-MD |
N/mm2 |
130 | 130 | 130 | 130 |
130 |
DIN
53 455 | |
|
-TD |
N/mm2 |
130 | 130 | 130 | 130 |
130 |
DIN
53 455 | ||
|
Elongation at break |
-MD |
% |
50 | 50 | 50 | 50 |
50 |
DIN
53 455 | |
|
-TD |
% |
50 | 50 | 50 | 50 |
50 |
DIN
53 455 | ||
|
shrinkage |
150℃ 15min |
-MD |
% |
2.5 | 2.5 | 2.5 | 2.5 | 2.5 |
BMS
TT 11 |
|
-TD |
% |
0.5 | 0.5 | 0.5 | 0.5 | 0.5 |
BMS
TT 11 | ||
|
Haze |
A |
% |
98 | 98 | 98 | 98 |
98 |
ASTM D 1003 | |
|
Light Transmit (Y) |
A |
% |
45±8 | 25±8 | 22±8 | 17±8 | 14±8 | ASTM D 1003 | |
|
Gloss |
60° |
% |
33±3 | 31±3 | 23±3 | 21±3 |
17±3 |
ASTM D 2457 |
|
Product data sheet for Silicone PET film
|
Item |
Unit |
Type |
Method | ||||
SFC |
|||||||
| Feature | clean subtract and uniform coating ,good bonding between silicone and film ,uniform and steady of peel force ,high adhesive residue ,low peel force aging and good solvent resistance to suitable for water and solvent base adhesive | ||||||
| Application | silicone coated on pet film to applied in adhesive type, high speed of auto pasted label and adhesive type for eletronic products and release liner for MLCC | ||||||
|
Thicknesss |
-MD |
μm |
12 |
25 |
38 |
DIN
53 370 | |
|
Tensile strength |
-MD |
N/mm2 |
150 | 150 | 150 |
DIN
53 455 | |
|
-TD |
N/mm2 |
150 | 150 | 150 |
DIN
53 455 | ||
|
Elongation at break |
-MD |
% |
60 | 60 | 60 |
DIN
53 455 | |
|
-TD |
% |
60 | 60 | 60 |
DIN
53 455 | ||
|
shrinkage |
150℃ 15min |
-MD |
% |
1.5 | 1.5 | 1.5 |
BMS
TT 11 |
|
-TD |
% |
0.3 | 0.3 | 0.3 |
BMS
TT 11 | ||
|
Peel force |
180° |
G/inch |
10 | 10 | 10 |
ASTM D 1003 | |
|
Haze |
A |
% |
3.0 | 3.8 | 5.0 | ASTM D 1003 | |
|
Gloss |
60° |
% |
120 | 120 |
120 |
ASTM D 2457 |
|
*the products data sheet is just for your reference and the above are some parts of